TI Self-assembly, metal binding ability, and magnetic properties of dinickel(II) and dicobalt(II) triple mesocates
SO CrystEngComm
JI CrystEngComm
PY 2012
BP 5639
EP 5648
VL 14
IS 17
DI 10.1039/c2ce25434d
LA English
AB Two metallacyclic complexes of general formula Na-8[(M2L3)-L-II]center dot xH(2)O [M = Ni (4) and Co (5) with x = 15 (4) and 17 (5)] have been self-assembled in aqueous solution from N,N'-1,3-phenylenebis(oxamic acid) (H4L) and M2+ ions in a ligand/metal molar ratio of 3 : 2 in the presence of NaOH acting as base. X-Ray structural analyses of 4 and 5 show triple-stranded, dinuclear anions of the meso-helicate-type (so-called mesocates) with C-3h molecular symmetry. The two octahedral metal-tris(oxamate) moieties of opposite chiralities (Delta, Lambda form) are connected by three m-phenylene spacers at intermetallic distances of 6.822(2) (4) and 6.868(2) angstrom (5) to give a metallacryptand core. In the crystal lattice, the binding of these heterochiral dinickel(II) and dicobalt(II) triple mesocates to sodium(I) ions leads to oxamato-bridged heterobimetallic three-dimensional open-frameworks with a hexagonal diamond architecture having small pores of 17.566(4) (4) and 17.640(2) angstrom (5) in diameter where the crystallization water molecules and the sodium(I) countercations are hosted. Variable temperature (2.0-300 K) magnetic susceptibility measurements reveal relatively anisotropic S = 2 Ni-2(II) (4) and S = 3 Co-2(II) (5) ground states resulting from the moderate to weak intramolecular ferromagnetic coupling between the two high-spin Ni-II (S-Ni = 1) or Co-II (S-Co = 3/2) ions across the m-phenylenediamidate bridges [J = +3.6 (4) and +1.1 cm(-1) (5); H = -JS(1)center dot S-2]. A simple molecular orbital analysis of the electron exchange interaction identifies the p-type pathways of the meta-substituted phenylene spacers involving the d(z2) and d(x2-y2) pairs of magnetic orbitals of the two trigonally distorted octahedral high-spin M-II ions (M = Ni and Co) as responsible for the overall ferromagnetic coupling observed in 4 and 5 in agreement with a spin polarization mechanism. The decrease of the overall ferromagnetic coupling from 4 to 5 is in turn explained by the additional antiferromagnetic exchange contribution involving the d(xy) pair of magnetic orbitals of the two trigonally distorted octahedral high-spin Co-II ions across the sigma-type pathway of the meta-substituted phenylene spacers.
ER